General Properties Alloy 410 is a hardenable, straight-chromium stainless steel which combines the superior wear resistance of high carbon alloys with the excellent corrosion resistance of chromium stainless steels. Oil quenching this alloy from temperatures between 1800°F to 1950°F (982-1066°C) produces the highest strength and/or wear resistance as well as corrosion resistance. ...

General Properties Alloys 321 (S32100) and 347 (S34700) are stabilized stainless steels which offer as their main advantage an excellent resistance to intergranular corrosion following exposure to temperatures in the chromium carbide precipitation range from 800 to 1500°F (427 to 816°C). Alloy 321 is stabilized against chromium carbide formation by the addition of titanium. Alloy 347 is ...

General Properties Alloys 317LMN and 317L are molybdenum-bearing austenitic stainless steels with greatly increased resistance to chemical attack as compared to the conventional chromium-nickel austenitic stainless steels such as Alloy 304. In addition, 317LMN and 317L alloys offer higher creep, stress-to-rupture, and tensile strengths at elevated temperatures than conventional stainless ...

General Properties Alloys 316 (UNS S31600), 316L (S31603), and 317L (S31703) are molybdenum-bearing austenitic stainless steels which are more resistant to general corrosion and pitting/crevice corrosion than the conventional chromium-nickel austenitic stainless steels such as Alloy 304. These alloys also offer higher creep, stress-to-rupture, and tensile strength at elevated temperatures. ...

General Properties Alloy 309/309S and Alloy 310/310S austenitic stainless steels are typically used for elevated temperature applications. Their high chromium and nickel contents provide comparable corrosion resistance, superior resistance to oxidation, and the retention of a larger fraction of room temperature strength than the common austenitic Alloy 304. Applications Higher alloyed ...

Alloy 17-4PH is a precipitation hardening martensitic stainless steel with Cu and Nb/Cb additions. The grade combines high strength, hardness (up to 572°F / 300°C), and corrosion resistance. Mechanical properties can be optimized with heat treatment. Very high yield strength up to 1100-1300 MPa (160-190 ksi) can be achieved. The grade should not be used at temperatures above ...

Grade 0Cr18Ni9,1Cr18Ni9,304,AISI304,SUS304,1.4301 （X5CrNi18-10） 304H 304L(Ni<8.5%),AISI304L(Ni<8.5%),304/304L,AISI304/304L,1.4307（X2CrNi18-9） 00Cr19Ni10,304L (Ni>=8.5%),SUS304L 0Cr19Ni10NbN 1Cr18Ni9Ti,1.4541（X6CrNiTi18-10） Adopting standards GB/T4237,ASTM,ASME,JIS G4304,EN10028 ASTM,ASME ASTM,ASME ,Q/TX3119-2005,EN 10028 GB/T4237 ,Q/140000 ...

Chinese Japanese American UK Germany French Russia GB1220-92[84] JIS AISI BS 970 Part4 DIN 17440 NFA35-572 TOCT5632 GB3220-92[84] UNS BS1449 Part2 DIN 17224 NFA35-576~582 NFA35-584 1Cr17Mn6Ni5N SUS201 201 -- -- -- -- 1Cr18Mn8Ni5N SUS202 202 -- -- -- 12×17.T9AH4 -- -- ...